PBT(聚对苯二甲酸丁二醇酯#聚酯)/1200M/台湾长春
用途： 合胶塑料、扣件组具、电脑键盘、文具外壳、旋钮开关。
材料特性：流动性能、成型性良好、表面光泽度佳。
重要参数： 密度:1.31 g/cm3 吸水率:0.06 % 成型收缩率:1.4 % 缺口冲击强度:5 拉伸强度:550 MPa 弯曲强度:800 MPa 硬度:87.5 热变形温度:60 ℃
生产厂商：台湾长春
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 吸水率 | --- | ASTM D-570 | 0.06 | % |
| 物理性能 | 成型收缩率 | --- | ASTM D-955 | 0.8-2.0 | % |
| 比重 | --- | ASTM D-792 | 1.30-1.32 | --- | |
| 玻璃纤维含量 | --- | Ash | 0 | % | |
| 机械性能 | 引张强度 | --- | ASTM D-638 | 500-600 | Kg/cm2 |
| 引张伸长率 | --- | ASTM D-638 | 50-90 | % | |
| 挠曲强度 | --- | ASTM D-790 | 750-850 | Kg/cm2 | |
| 挠曲弹性率 | --- | ASTM D-790 | 22000 | Kg/cm2 | |
| IZOD冲击强度 | --- | ASTM D-256 | 4.5-5.5 | Kg.cm/cm | |
| 洛氏硬度 | --- | ASTM D-785 | 85-90 | M-Scale | |
| 电气性能 | 诱电率 | 60Hz | ASTM D-150 | 3.3 | --- |
| 诱电正接 | 60Hz | ASTM D-150 | 0.001 | --- | |
| 体积电阻率 | --- | ASTM D-257 | >1016 | Ω.cm | |
| 表面电阻率 | --- | ASTM D-257 | >1014 | Ω | |
| 绝缘破坏强度 | --- | ASTM D-149 | 20 | KV/mm | |
| 耐电弧性 | --- | ASTM D-495 | 120 | sec | |
| 热 性 能 | 耐燃性 | --- | UL 94 | HB | --- |
| 热变形温度 | 4.6Kg/cm2 | ASTM D-648 | 155 | ℃ | |
| 线膨胀系数 | --- | ASTM D-696 | 9 | 10-5cm/cm℃ | |
| 熔点 | --- | DSC | 225 | ℃ | |
| 热变形温度 | 18.6Kg/cm2 | ASTM D-648 | 60 | ℃ | |